- 密度 [g/cm3]: 1.22
- 吸水率 [%]: 0.4
- 缺口沖擊強度: 0.32
- 斷裂伸長率 [%]: 103
- 彎曲強度 [MPa]: 62.1
- 彎曲模量 [MPa]: 4.14
- 硬度: 118.0
- 熱變形溫度 [℃]: 232.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 - 1.65 g/cc | 0.0441 - 0.0596 lb/in3 | Average value: 1.43 g/cc Grade Count:34 |
| Filler Content | 10.0 - 50.0 % | 10.0 - 50.0 % | Average value: 31.0 % Grade Count:21 |
| Water Absorption | 0.400 - 1.00 % | 0.400 - 1.00 % | Average value: 0.700 % Grade Count:14 |
| Linear Mold Shrinkage | 0.00100 - 0.0130 cm/cm | 0.00100 - 0.0130 in/in | Average value: 0.00371 cm/cm Grade Count:30 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00400 - 0.0150 cm/cm | 0.00400 - 0.0150 in/in | Average value: 0.00812 cm/cm Grade Count:8 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 118 - 121 | 118 - 121 | Average value: 120 Grade Count:8 |
| Tensile Strength, Ultimate | 62.1 - 228 MPa | 9000 - 33000 psi | Average value: 161 MPa Grade Count:34 |
| Elongation at Break | 1.00 - 5.00 % | 1.00 - 5.00 % | Average value: 2.95 % Grade Count:32 |
| Modulus of Elasticity | 4.83 - 17.2 GPa | 700 - 2500 ksi | Average value: 10.3 GPa Grade Count:25 |
| Flexural Yield Strength | 103 - 331 MPa | 15000 - 48000 psi | Average value: 244 MPa Grade Count:34 |
| Flexural Modulus | 4.14 - 15.5 GPa | 600 - 2250 ksi | Average value: 9.47 GPa Grade Count:34 |
| Izod Impact, Notched | 0.320 - 1.71 J/cm | 0.600 - 3.20 ft-lb/in | Average value: 0.912 J/cm Grade Count:33 |
| Izod Impact, Unnotched | 2.67 - 13.3 J/cm | 5.00 - 25.0 ft-lb/in | Average value: 7.52 J/cm Grade Count:25 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+14 - 1.00e+16 ohm-cm | 1.00e+14 - 1.00e+16 ohm-cm | Average value: 2.51e+15 ohm-cm Grade Count:20 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 232 - 266 °C | 450 - 510 °F | Average value: 256 °C Grade Count:18 |
| Deflection Temperature at 1.8 MPa (264 psi) | 194 - 260 °C | 381 - 500 °F | Average value: 245 °C Grade Count:32 |
| Flammability, UL94 | HB | HB | Grade Count:21 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 271 - 293 °C | 520 - 560 °F | Average value: 283 °C Grade Count:11 |
| Melt Temperature | 277 - 310 °C | 530 - 590 °F | Average value: 289 °C Grade Count:18 |
| Mold Temperature | 65.6 - 107 °C | 150 - 225 °F | Average value: 87.3 °C Grade Count:27 |
| Drying Temperature | 79.4 - 107 °C | 175 - 225 °F | Average value: 82.0 °C Grade Count:18 |
| Dry Time | 4.00 hour | 4.00 hour | Average value: 4.00 hour Grade Count:13 |
| Moisture Content | 0.200 % | 0.200 % | Average value: 0.200 % Grade Count:14 |
| Dew Point | -17.8 °C | 0.000 °F | Average value: -17.8 °C Grade Count:14 |
| Injection Pressure | 68.9 - 124 MPa | 10000 - 18000 psi | Average value: 99.2 MPa Grade Count:23 |