- 密度 [g/cm3]: 1.08
- 吸水率 [%]: 0.3
- 缺口沖擊強度: 0.267
- 拉伸強度 [MPa]: 46.0
- 斷裂伸長率 [%]: 11.7
- 彎曲強度 [MPa]: 48.3
- 彎曲模量 [MPa]: 1.69
- 硬度: 113.0
- 熱變形溫度 [℃]: 195.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 - 1.60 g/cc | 0.0390 - 0.0578 lb/in3 | Average value: 1.19 g/cc Grade Count:40 |
| Water Absorption | 0.300 - 8.50 % | 0.300 - 8.50 % | Average value: 1.29 % Grade Count:20 |
| Moisture Absorption at Equilibrium | 2.60 - 2.80 % | 2.60 - 2.80 % | Average value: 2.73 % Grade Count:3 |
| Water Absorption at Saturation | 7.00 - 8.50 % | 7.00 - 8.50 % | Average value: 7.88 % Grade Count:4 |
| Linear Mold Shrinkage | 0.00300 - 0.0210 cm/cm | 0.00300 - 0.0210 in/in | Average value: 0.0121 cm/cm Grade Count:37 |
| Linear Mold Shrinkage, 6.35 mm section | 0.0140 - 0.0200 cm/cm | 0.0140 - 0.0200 in/in | Average value: 0.0160 cm/cm Grade Count:5 |
| Linear Mold Shrinkage, Transverse | 0.00500 - 0.0140 cm/cm | 0.00500 - 0.0140 in/in | Average value: 0.00975 cm/cm Grade Count:4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 85.0 - 98.0 | 85.0 - 98.0 | Average value: 91.3 Grade Count:3 |
| Hardness, Rockwell R | 113 - 120 | 113 - 120 | Average value: 118 Grade Count:15 |
| Tensile Strength, Ultimate | 48.3 - 215 MPa | 7000 - 31200 psi | Average value: 89.3 MPa Grade Count:30 |
| 41.0 - 59.0 MPa @Temperature 60.0 - 120 °C | 5950 - 8560 psi @Temperature 140 - 248 °F | Average value: 49.7 MPa Grade Count:1 | |
| Tensile Strength, Yield | 46.0 - 145 MPa | 6670 - 21000 psi | Average value: 84.9 MPa Grade Count:13 |
| Elongation at Break | 3.50 - 70.0 % | 3.50 - 70.0 % | Average value: 13.4 % Grade Count:31 |
| Elongation at Yield | 4.00 - 100 % | 4.00 - 100 % | Average value: 48.0 % Grade Count:3 |
| Modulus of Elasticity | 2.41 - 4.14 GPa | 350 - 600 ksi | Average value: 3.60 GPa Grade Count:15 |
| Flexural Yield Strength | 11.7 - 193 MPa | 1700 - 28000 psi | Average value: 116 MPa Grade Count:34 |
| Flexural Modulus | 1.69 - 14.5 GPa | 245 - 2100 ksi | Average value: 3.65 GPa Grade Count:40 |
| 0.750 - 1.75 GPa @Temperature 60.0 - 120 °C | 109 - 254 ksi @Temperature 140 - 248 °F | Average value: 1.22 GPa Grade Count:1 | |
| Izod Impact, Notched | 0.267 - 7.88 J/cm | 0.500 - 14.8 ft-lb/in | Average value: 0.812 J/cm Grade Count:39 |
| 0.250 - 0.300 J/cm @Temperature -40.0 - -20.0 °C | 0.468 - 0.562 ft-lb/in @Temperature -40.0 - -4.00 °F | Average value: 0.275 J/cm Grade Count:1 | |
| Izod Impact, Unnotched | 4.32 - 18.7 J/cm | 8.09 - 35.0 ft-lb/in | Average value: 10.3 J/cm Grade Count:15 |
| Izod Impact, Notched (ISO) | 5.00 - 5.00 kJ/m2 @Temperature -30.0 - -30.0 °C | 2.38 - 2.38 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 5.00 kJ/m2 Grade Count:1 |
| Izod Impact, Unnotched (ISO) | NB - NB @Temperature -30.0 - -30.0 °C | NB - NB @Temperature -22.0 - -22.0 °F | Grade Count:1 |
| Charpy Impact Unnotched | 3.50 - 30.0 J/cm2 | 16.7 - 143 ft-lb/in2 | Average value: 13.2 J/cm2 Grade Count:3 |
| >= 30.0 J/cm2 @Temperature -40.0 - -20.0 °C | >= 143 ft-lb/in2 @Temperature -40.0 - -4.00 °F | Average value: 30.0 J/cm2 Grade Count:1 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+14 - 1.00e+16 ohm-cm | 1.00e+14 - 1.00e+16 ohm-cm | Average value: 2.23e+15 ohm-cm Grade Count:15 |
| Surface Resistance | 1.00e+13 - 1.00e+14 ohm | 1.00e+13 - 1.00e+14 ohm | Average value: 2.80e+13 ohm Grade Count:5 |
| Dielectric Constant | 3.60 - 3.70 | 3.60 - 3.70 | Average value: 3.65 Grade Count:4 |
| Dielectric Strength | 13.8 - 120 kV/mm | 350 - 3050 kV/in | Average value: 58.3 kV/mm Grade Count:5 |
| Comparative Tracking Index | 500 - 600 V | 500 - 600 V | Average value: 533 V Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 15.0 - 100 μm/m-°C | 8.33 - 55.6 μin/in-°F | Average value: 61.1 μm/m-°C Grade Count:7 |
| Thermal Conductivity | 0.245 - 0.259 W/m-K | 1.70 - 1.80 BTU-in/hr-ft2-°F | Average value: 0.255 W/m-K Grade Count:3 |
| Melting Point | 249 - 275 °C | 480 - 527 °F | Average value: 257 °C Grade Count:11 |
| Maximum Service Temperature, Air | 80.0 - 200 °C | 176 - 392 °F | Average value: 133 °C Grade Count:3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 195 - 262 °C | 383 - 504 °F | Average value: 225 °C Grade Count:24 |
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 - 257 °C | 147 - 495 °F | Average value: 105 °C Grade Count:38 |
| Vicat Softening Point | 242 - 257 °C | 468 - 495 °F | Average value: 251 °C Grade Count:3 |
| Flammability, UL94 | HB - V-2 | HB - V-2 | Grade Count:20 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 270 - 293 °C | 518 - 560 °F | Average value: 285 °C Grade Count:9 |
| Melt Temperature | 260 - 299 °C | 500 - 570 °F | Average value: 281 °C Grade Count:19 |
| Mold Temperature | 40.0 - 107 °C | 104 - 225 °F | Average value: 80.7 °C Grade Count:25 |
| Drying Temperature | 73.9 - 100 °C | 165 - 212 °F | Average value: 81.9 °C Grade Count:14 |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Average value: 3.50 hour Grade Count:10 |
| 2.00 - 4.00 hour @Temperature 71.1 - 79.4 °C | 2.00 - 4.00 hour @Temperature 160 - 175 °F | Average value: 3.00 hour Grade Count:4 | |
| Moisture Content | 0.200 % | 0.200 % | Average value: 0.200 % Grade Count:8 |
| Dew Point | -17.8 °C | 0.000 °F | Average value: -17.8 °C Grade Count:7 |
| Injection Pressure | 4.96 - 124 MPa | 720 - 18000 psi | Average value: 66.1 MPa Grade Count:17 |
| Back Pressure | 0.000 - 1.72 MPa | 0.000 - 250 psi | Average value: 0.603 MPa Grade Count:4 |
| Shot Size | 30.0 - 80.0 % | 30.0 - 80.0 % | Average value: 55.0 % Grade Count:4 |
| Screw Speed | 20.0 - 100 rpm | 20.0 - 100 rpm | Average value: 60.0 rpm Grade Count:4 |