- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 1.9
- 拉伸強度 [MPa]: 80.0
- 彎曲模量 [MPa]: 2.80
- 熱變形溫度 [℃]: 220.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in3 | ASTM D792 | ||
| Water Absorption | 1.9 % | 1.9 % | 24h in H2O; sim. ISO 62 | ||
| Water Absorption at Saturation | 9.0 % | 9.0 % | sim. ISO 62 | ||
| Loss On Ignition | 28 % | 28 % | ASTM D2863 | ||
| Viscosity Measurement | 50 | 50 | relative viscosity (formic acid); ASTM D789 | ||
| Linear Mold Shrinkage, Flow | 0.013 cm/cm | 0.013 in/in | parallel; Nilit | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | ASTM D638 | ||
| Elongation at Break | 30 % | 30 % | ASTM D638 | ||
| Tensile Modulus | 2.95 GPa | 428 ksi | ASTM D638 | ||
| Flexural Strength | 115 MPa | 16700 psi | ASTM D790 | ||
| Flexural Modulus | 2.80 GPa | 406 ksi | ASTM D790 | ||
| Charpy Impact Unnotched | NB | NB | ISO 179 | ||
| Charpy Impact, Notched | 0.650 J/cm2 | 3.09 ft-lb/in2 | ISO 179 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 18.0 kV/mm @Thickness 2.00 mm | 457 kV/in @Thickness 0.0787 in | ASTM D149 | ||
| Comparative Tracking Index | >= 600 V | >= 600 V | UL 746 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ASTM D648 | ||
| Vicat Softening Point | 235 °C | 455 °F | 49 N; ASTM D1525 | ||
| 245 °C | 473 °F | 9.8 N; ASTM D1525 | |||
| Flammability, UL94 | V-2 @Thickness 0.800 mm | V-2 @Thickness 0.0315 in | |||
| V-2 @Thickness 1.60 mm | V-2 @Thickness 0.0630 in | ||||
| Descriptive Properties | |||||
| Heat Resistance - Ball Test | OK | at 125°C, IEC 309 | |||
| OK | at 165°C, IEC 309 | ||||