- 密度 [g/cm3]: 1.2
- 熱變形溫度 [℃]: 190.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in3 | ±0.02 g/cm3; DIN 53479 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 75.0 MPa @Temperature 23.0 °C | 10900 psi @Temperature 73.4 °F | ISO 527-2/5 | ||
| Elongation at Break | 5.5 % @Temperature 23.0 °C | 5.5 % @Temperature 73.4 °F | ISO 527-2/5 | ||
| Tensile Modulus | 4.00 GPa @Temperature 23.0 °C | 580 ksi @Temperature 73.4 °F | ISO 527-2/1 | ||
| Charpy Impact Unnotched | 6.40 J/cm2 @Temperature -30.0 °C | 30.5 ft-lb/in2 @Temperature -22.0 °F | ISO 179 | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179 | |||
| Charpy Impact, Notched | 0.240 J/cm2 @Temperature -30.0 °C | 1.14 ft-lb/in2 @Temperature -22.0 °F | ISO 179 | ||
| 0.300 J/cm2 @Temperature 23.0 °C | 1.43 ft-lb/in2 @Temperature 73.4 °F | ISO 179 | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 | ||
| Dielectric Strength | 45.0 kV/mm | 1140 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.30 @Frequency 1.00e+6 Hz | 0.30 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 600 V | 600 V | Solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 243 °C | 469 °F | ISO 3146 | ||
| Maximum Service Temperature, Air | 115 °C | 239 °F | Continuous (GTP 50% Tensile); IEC 60216 | ||
| 200 °C | 392 °F | Short Time; IEC 60216 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 190 °C | 374 °F | Unannealed; ISO 75-2/B | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | Unannealed; ISO 75-2/A | ||
| Flammability, UL94 | V-0 @Thickness 0.400 mm | V-0 @Thickness 0.0157 in | ALL; Internal Method | ||
| Glow Wire Test | 725 °C @Thickness 0.800 mm | 1340 °F @Thickness 0.0315 in | uncolored material; Ignition Temperature; IEC 60695-2-13 | ||
| 960 °C @Thickness 0.800 mm | 1760 °F @Thickness 0.0315 in | Flammability Index; uncolored material; IEC 60695-2-12 | |||
| Descriptive Properties | |||||
| Additive | Heat Stabilizer | ||||
| Features | Flame Retardant | ||||
| Good Flow | |||||
| Halogen Free | |||||
| Heat Stabilized | |||||
| Low (to None) Phosphorus Content | |||||
| Forms | Pellets | ||||
| Generic Material | Nylon 66/6 | ||||
| Generic Name | Polyamide 66/6 Copolymer (Nylon 66/6) | ||||
| Regional Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| RoHS Compliance | RoHS Compliant | ||||