- 熔體流動速率 [g/10min]: 3.0
- 密度 [g/cm3]: 1.36
- 彎曲模量 [MPa]: 3.80
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in3 | |
| Viscosity Measurement | 0.74 - 0.82 | 0.74 - 0.82 | |
| Linear Mold Shrinkage | 0.0074 cm/cm | 0.0074 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0082 cm/cm | 0.0082 in/in | |
| Melt Flow | 3.0 g/10 min @Load 0.325 kg, Temperature 270 °C | 3.0 g/10 min @Load 0.716 lb, Temperature 518 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 70.0 MPa | 10200 psi | |
| Elongation at Break | 6.0 % | 6.0 % | |
| Tensile Modulus | 5.25 GPa | 761 ksi | |
| Flexural Strength | 108 MPa | 15700 psi | |
| Flexural Modulus | 3.80 GPa | 551 ksi | |
| Charpy Impact Unnotched | 3.60 J/cm2 @Temperature -20.0 °C | 17.1 ft-lb/in2 @Temperature -4.00 °F | |
| 4.60 J/cm2 @Temperature 23.0 °C | 21.9 ft-lb/in2 @Temperature 73.4 °F | ||
| Charpy Impact, Notched | 0.200 J/cm2 @Temperature -20.0 °C | 0.952 ft-lb/in2 @Temperature -4.00 °F | |
| 0.400 J/cm2 @Temperature 23.0 °C | 1.90 ft-lb/in2 @Temperature 73.4 °F | ||
| Thermal Properties | Metric | English | Comments |
| Melting Point | 260 °C | 500 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | |
| Vicat Softening Point | 208 °C | 406 °F | B |
| Flammability, UL94 | HB | HB | |
| Glow Wire Test | 650 °C | 1200 °F | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 280 - 310 °C | 536 - 590 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | 0.20 % | 0.20 % | |
| Injection Pressure | 70.0 - 120 MPa | 10200 - 17400 psi | |