- 密度 [g/cm3]: 1.67
- 彎曲模量 [MPa]: 18.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.67 g/cc | 0.0603 lb/in3 | ISO 1183 | ||
| Viscosity Test | 120 cm3/g | 120 cm3/g | ISO 307, 1157, 1628 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 270 MPa | 39200 psi | 5mm/min; ISO 527-2/1A | ||
| Tensile Strength | 150 MPa @Temperature 80.0 °C | 21800 psi @Temperature 176 °F | ISO 527-1, -2 | ||
| Elongation at Break | 2.00 % | 2.00 % | 5mm/min; ISO 527-2/1A | ||
| 2.30 % @Temperature 80.0 °C | 2.30 % @Temperature 176 °F | ISO 527-1, -2 | |||
| Tensile Modulus | 19.5 GPa | 2830 ksi | 1mm/min; ISO 527-2/1A | ||
| 10.0 GPa @Temperature 80.0 °C | 1450 ksi @Temperature 176 °F | ISO 527-1, -2 | |||
| Flexural Strength | 450 MPa | 65300 psi | ISO 178 | ||
| 290 MPa @Temperature 80.0 °C | 42100 psi @Temperature 176 °F | ISO 178 | |||
| Flexural Modulus | 18.0 GPa | 2610 ksi | ISO 178 | ||
| 13.0 GPa @Temperature 80.0 °C | 1890 ksi @Temperature 176 °F | ISO 178 | |||
| Izod Impact, Unnotched (ISO) | 90.0 kJ/m2 | 42.8 ft-lb/in2 | ISO 180/1U | ||
| 80.0 kJ/m2 @Temperature -30.0 °C | 38.1 ft-lb/in2 @Temperature -22.0 °F | ISO 180/1U | |||
| Charpy Impact Unnotched | 9.50 J/cm2 | 45.2 ft-lb/in2 | ISO 179/1eU | ||
| 8.50 J/cm2 @Temperature -30.0 °C | 40.4 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 5.00 J/cm2 | 23.8 ft-lb/in2 | ISO 179/1eA | ||
| 4.50 J/cm2 @Temperature -30.0 °C | 21.4 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | |||
| Puncture Energy | 31.0 J @Temperature -30.0 °C | 22.9 ft-lb @Temperature -22.0 °F | ISO 6603-2 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 240 °C | 464 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 8.0 MPa | 220 °C | 428 °F | ISO 75-1, -2 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 70.0 - 80.0 °C | 158 - 176 °F | |||
| 80.0 - 100 °C | 176 - 212 °F | Cavity temperature | |||
| Feed Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| Zone 1 | 285 - 295 °C | 545 - 563 °F | |||
| Zone 2 | 290 - 300 °C | 554 - 572 °F | |||
| Zone 3 | 300 - 310 °C | 572 - 590 °F | |||
| Zone 4 | 300 - 315 °C | 572 - 599 °F | |||
| Die Temperature | 300 - 315 °C | 572 - 599 °F | |||
| Melt Temperature | 300 - 315 °C | 572 - 599 °F | |||
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | |||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |||
| Moisture Content | 0.150 % | 0.150 % | Necessary low maximum residual | ||
| Injection Pressure | 120 - 150 MPa | 17400 - 21800 psi | |||
| Hold Pressure | 50.0 - 80.0 MPa | 7250 - 11600 psi | |||
| Back Pressure | 3.00 MPa | 435 psi | |||
| Screw Speed | 25.0 rpm @Diameter 75.0 mm | 25.0 rpm @Diameter 2.95 in | |||
| 35.0 rpm @Diameter 55.0 mm | 35.0 rpm @Diameter 2.17 in | ||||
| 50.0 rpm @Diameter 40.0 mm | 50.0 rpm @Diameter 1.57 in | ||||
| Hot-Working Temperature | 300 - 315 °C | 572 - 599 °F | |||
| Descriptive Properties | |||||
| Injection speed | medium | ||||