- 密度 [g/cm3]: 1.14
- 吸水率 [%]: 8.5
- 缺口沖擊強度: 5.0
- 拉伸強度 [MPa]: 90.0
- 彎曲模量 [MPa]: 3.00
- 硬度: 118.0
- 熱變形溫度 [℃]: 100.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in3 | ISO 1183 |
| Moisture Absorption at Equilibrium | 2.8 % | 2.8 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 8.5 % | 8.5 % | ISO 62 |
| Linear Mold Shrinkage | 0.014 - 0.018 cm/cm | 0.014 - 0.018 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 118 | 118 | |
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | ISO 527 |
| Elongation at Break | 25 % | 25 % | ISO 527 |
| Flexural Strength | 140 MPa | 20300 psi | ISO 178 |
| Flexural Modulus | 3.00 GPa | 435 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m2 | 2.38 ft-lb/in2 | ISO 180 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 3.6 @Frequency 1.00e+6 Hz | 3.6 @Frequency 1.00e+6 Hz | IEC 60250 |
| Dielectric Strength | 120 kV/mm | 3050 kV/in | IEC 60250 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 256 °C | 493 °F | ISO 11357 |
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | Continuous use |
| 200 °C | 392 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75 |
| Flammability, UL94 | V-2 @Thickness 3.00 mm | V-2 @Thickness 0.118 in | |
| Glow Wire Test | 750 °C | 1380 °F | GWFI; IEC 60695 |