- 密度 [g/cm3]: 1.12
- 彎曲模量 [MPa]: 2.80
- 熱變形溫度 [℃]: 195.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in3 | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | <= 75.0 MPa | <= 10900 psi | ISO/R527 |
| Elongation at Yield | 5.0 % | 5.0 % | ISO/R527 |
| Flexural Strength | <= 120 MPa | <= 17400 psi | ISO 178 |
| Flexural Modulus | 2.80 GPa @Temperature 23.0 °C | 406 ksi @Temperature 73.4 °F | ISO 178 |
| Charpy Impact, Notched | 1.20 J/cm2 @Temperature 23.0 °C | 5.71 ft-lb/in2 @Temperature 73.4 °F | ISO 179 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | >= 195 °C @Load 5.001 kg | >= 383 °F @Load 11.03 lb | 50°C/h; ISO 306 |