- 熔體流動速率 [g/10min]: 5.0
- 密度 [g/cm3]: 1.37
- 彎曲模量 [MPa]: 8.32
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in3 | |
| Viscosity Measurement | 0.36 - 0.37 | 0.36 - 0.37 | |
| Linear Mold Shrinkage | 0.0037 cm/cm | 0.0037 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0036 cm/cm | 0.0036 in/in | |
| Melt Flow | 5.0 g/10 min @Load 0.325 kg, Temperature 270 °C | 5.0 g/10 min @Load 0.716 lb, Temperature 518 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 105 MPa | 15200 psi | |
| Elongation at Break | 3.0 % | 3.0 % | |
| Tensile Modulus | 8.56 GPa | 1240 ksi | |
| Flexural Strength | 155 MPa | 22500 psi | |
| Flexural Modulus | 8.32 GPa | 1210 ksi | |
| Charpy Impact Unnotched | 3.50 J/cm2 @Temperature 23.0 °C | 16.7 ft-lb/in2 @Temperature 73.4 °F | |
| 3.80 J/cm2 @Temperature -20.0 °C | 18.1 ft-lb/in2 @Temperature -4.00 °F | ||
| Charpy Impact, Notched | 0.400 J/cm2 @Temperature -20.0 °C | 1.90 ft-lb/in2 @Temperature -4.00 °F | |
| 0.500 J/cm2 @Temperature 23.0 °C | 2.38 ft-lb/in2 @Temperature 73.4 °F | ||
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | |
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | |
| Comparative Tracking Index | 550 V | 550 V | |
| Thermal Properties | Metric | English | Comments |
| Flammability, UL94 | V-0 | V-0 | |
| Glow Wire Test | 960 °C | 1760 °F | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 260 - 280 °C | 500 - 536 °F | |
| Mold Temperature | 50.0 - 70.0 °C | 122 - 158 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | 0.15 % | 0.15 % | |
| Injection Pressure | 70.0 - 100 MPa | 10200 - 14500 psi | |