- 熔體流動速率 [g/10min]: 10.0
- 密度 [g/cm3]: 1.16
- 彎曲模量 [MPa]: 3.30
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in3 | |
| Viscosity Measurement | 0.75 - 0.87 | 0.75 - 0.87 | |
| Linear Mold Shrinkage | 0.0075 cm/cm | 0.0075 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0087 cm/cm | 0.0087 in/in | |
| Melt Flow | 10 g/10 min @Load 0.325 kg, Temperature 270 °C | 10 g/10 min @Load 0.716 lb, Temperature 518 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 80.0 MPa | 11600 psi | |
| Elongation at Break | 6.0 % | 6.0 % | |
| Tensile Modulus | 3.65 GPa | 529 ksi | |
| Flexural Strength | 125 MPa | 18100 psi | |
| Flexural Modulus | 3.30 GPa | 479 ksi | |
| Charpy Impact Unnotched | 8.00 J/cm2 @Temperature -20.0 °C | 38.1 ft-lb/in2 @Temperature -4.00 °F | |
| 8.50 J/cm2 @Temperature 23.0 °C | 40.4 ft-lb/in2 @Temperature 73.4 °F | ||
| Charpy Impact, Notched | 0.300 J/cm2 @Temperature -20.0 °C | 1.43 ft-lb/in2 @Temperature -4.00 °F | |
| 0.400 J/cm2 @Temperature 23.0 °C | 1.90 ft-lb/in2 @Temperature 73.4 °F | ||
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | |
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | |
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 262 °C | 504 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | |
| Vicat Softening Point | 215 °C | 419 °F | B |
| Flammability, UL94 | V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | |
| Glow Wire Test | 960 °C | 1760 °F | at 3 mm |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 260 - 280 °C | 500 - 536 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | 0.15 % | 0.15 % | |
| Injection Pressure | 70.0 - 100 MPa | 10200 - 14500 psi | |