- 拉伸強度 [MPa]: 80.0
- 彎曲模量 [MPa]: 2.50
- 熱變形溫度 [℃]: 180.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | ISO 527-1/2 |
| Elongation at Break | 35 % | 35 % | ISO 527-1/2 |
| Elongation at Yield | 3.9 % | 3.9 % | ISO 524-1/2 |
| Tensile Modulus | 3.00 GPa | 435 ksi | ISO 527-1/2 |
| Flexural Strength | 100 MPa | 14500 psi | ISO 178 |
| Flexural Modulus | 2.50 GPa | 363 ksi | ISO 178 |
| Charpy Impact, Notched | 0.500 J/cm2 | 2.38 ft-lb/in2 | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 245 °C | 473 °F | ISO 1135 7-1-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 180 °C | 356 °F | ISO 75/2Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75/2Af |
| Vicat Softening Point | 210 °C | 410 °F | ISO 306 |
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | |