- 拉伸強度 [MPa]: 165.0
- 彎曲模量 [MPa]: 8.15
- 熱變形溫度 [℃]: 235.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.28 g/cc | 1.28 g/cc | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 165 MPa | 23900 psi | ISO 527-1/2 |
| Elongation at Break | 3.3 % | 3.3 % | ISO 527-1/2 |
| Tensile Modulus | 10.3 GPa | 1490 ksi | ISO 527-1/2 |
| Flexural Strength | 240 MPa | 34800 psi | ISO 178 |
| Flexural Modulus | 8.15 GPa | 1180 ksi | ISO 178 |
| Charpy Impact Unnotched | 6.80 J/cm2 | 32.4 ft-lb/in2 | ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 245 °C | 473 °F | ISO 1135 7-1-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 235 °C | 455 °F | ISO 75/2Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ISO 75/2Af |
| Vicat Softening Point | 225 °C | 437 °F | ISO 306 |
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | |