- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 2.0
- 缺口沖擊強度: 0.4
- 拉伸強度 [MPa]: 72.0
- 斷裂伸長率 [%]: 89.0
- 彎曲模量 [MPa]: 2.372
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in3 | ASTM D792 |
| Water Absorption | 2.0 % | 2.0 % | ASTM D570 |
| Linear Mold Shrinkage | 0.015 cm/cm | 0.015 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 72.0 MPa | 10400 psi | ASTM D638 |
| Elongation at Break | 200 % | 200 % | ASTM D638 |
| Flexural Yield Strength | 89.0 MPa | 12900 psi | ASTM D790 |
| Flexural Modulus | 2.372 GPa | 344.0 ksi | ASTM D790 |
| Izod Impact, Notched | 0.400 J/cm | 0.749 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 199 °C | 390 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 250 °C | 482 °F | |
| Rear Barrel Temperature | 200 °C | 392 °F | |
| Middle Barrel Temperature | 230 °C | 446 °F | |
| Front Barrel Temperature | 250 °C | 482 °F | |
| Nozzle Temperature | 250 °C | 482 °F | |
| Mold Temperature | 80.0 °C | 176 °F | |
| Drying Temperature | 76.0 °C | 169 °F | |