- 熔體流動速率 [g/10min]: 0.4
- 密度 [g/cm3]: 0.948
- 拉伸強度 [MPa]: 19.0
- 彎曲模量 [MPa]: 0.700
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.948 g/cc | 0.0342 lb/in3 | ISO 1183 | ||
| Environmental Stress Crack Resistance | >= 5.0 hour @Pressure 0.800 MPa, Temperature 80.0 °C | >= 5.0 hour @Pressure 116 psi, Temperature 176 °F | ISO 13479 | ||
| Oxidative Induction Time (OIT) | >= 20 min @Temperature 200 °C | >= 20 min @Temperature 392 °F | EN 728 | ||
| Melt Flow | 0.40 g/10 min @Load 5.00 kg, Temperature 190 °C | 0.40 g/10 min @Load 11.0 lb, Temperature 374 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 19.0 MPa | 2760 psi | 50mm/min; ISO 527-2 | ||
| Elongation at Break | >= 600 % | >= 600 % | ISO 527-2 | ||
| Flexural Modulus | 0.700 GPa | 102 ksi | ISO 178 | ||
| Processing Properties | Metric | English | Comments | ||
| Middle Barrel Temperature | 180 - 210 °C | 356 - 410 °F | cylinder | ||
| Die Temperature | 200 - 210 °C | 392 - 410 °F | |||
| Melt Temperature | 200 - 220 °C | 392 - 428 °F | |||
| Head Temperature | 200 - 210 °C | 392 - 410 °F | |||
| Descriptive Properties | |||||
| Resistance To Rapid Crack Propagation (bar) | 7 | S4 test, Pc at 0°C, test pipe 250mm, SDR11, ISO 13477 | |||