- 密度 [g/cm3]: 0.936
- 拉伸強度 [MPa]: 22.0
- 彎曲模量 [MPa]: 0.680
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.936 g/cc | 0.0338 lb/in3 | Base Resin; ISO 1183 |
| Oxidative Induction Time (OIT) | >= 40 min | >= 40 min | 210°C; EN 728/AI cup |
| High Load Melt Index | 10 g/10 min @Load 21.6 kg, Temperature 190 °C | 10 g/10 min @Load 47.6 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 22.0000 MPa | 3190.83 psi | At 50 mm/min; ISO 527 |
| Elongation at Yield | 10 % | 10 % | ISO 527-2 |
| Tensile Modulus | 0.840 GPa | 122 ksi | ISO 527-2 |
| Flexural Modulus | 0.680 GPa | 98.6 ksi | At 2 mm/min; ISO 178 |