- 熔體流動速率 [g/10min]: 6.0
- 密度 [g/cm3]: 0.934
- 拉伸強度 [MPa]: 18.0
- 彎曲模量 [MPa]: 0.600
- 熱變形溫度 [℃]: 58.0
- 脆化溫度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.934 g/cc | 0.0337 lb/in3 | ASTM D1505 |
| ESCR 10% Igepal? | >= 4.0 hour | >= 4.0 hour | Ranked from 1 to 5 with 5 being the best; ASTM D1693 |
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 6.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 55 | 55 | ASTM D 2240 |
| Tensile Strength, Yield | 18.0 MPa | 2610 psi | At 50 mm/min; ASTM D6883 IV |
| Elongation at Yield | 13 % | 13 % | At 50 mm/min; ASTM D6883 IV |
| Tensile Modulus | 0.550 GPa | 79.8 ksi | ASTM D6883 IV |
| Flexural Modulus | 0.600 GPa | 87.0 ksi | At 2 mm/min; ASTM D790 |
| Dart drop Total Energy | 210.0 J/cm | 0.3934 ft-lb/mil | (-4oF/-20°C); ASTM D3763 |
| Dart Drop | 142 g/micron | 3610 g/mil | Instrumented Falling Weight (-4°F/-20°C); ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 58.0 °C | 136 °F | ASTM D648 |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D746 |