| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.924 g/cc | 0.924 g/cc | ASTM D792 |
| ESCR 100% Igepal? | 50 hour | 50 hour | Condition C; ASTM D1692 |
| Melt Index of Compound | 50 g/10 min | 50 g/10 min | Condition E; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 50 | 50 | ASTM D2240 |
| Tensile Strength, Yield | 11.0 MPa | 1600 psi | 2"/min; ASTM D638 |
| Elongation at Break | 175 % | 175 % | 2"/min; ASTM D638 |
| Flexural Modulus | 0.317 GPa | 46.0 ksi | at 1% secant modulus; ASTM D790 |
| Falling Dart Impact | 27.1 J | 20.0 ft-lb | -40°C; ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -71.0 °C | -95.8 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 122 °C | 252 °F | |