- 熔體流動(dòng)速率 [g/10min]: 0.7
- 密度 [g/cm3]: 0.93
- 拉伸強(qiáng)度 [MPa]: 18.6
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.930 g/cc | 0.0336 lb/in3 | ME 4425; ASTM D792 |
| 0.941 g/cc | 0.0340 lb/in3 | LE 4437; ASTM D792 | |
| Melt Flow | 0.70 g/10 min | 0.70 g/10 min | ME 4425; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | >= 18.6 MPa | >= 2700 psi | Heat Aging (7 days at 121°C); ASTM D412 |
| 20.7 MPa | 3000 psi | ASTM D412 | |
| Elongation at Break | <= 50 % | <= 50 % | Hot Creep Test (150°C, .2 MPa); ICEA T-28-562 |
| 315 % | 315 % | Heat Aging (7 days at 121°C); ASTM D412 | |
| 350 % | 350 % | ASTM D412 | |
| Tensile Set | <= 5.0 % | <= 5.0 % | Hot Creep Test (150°C,.2 MPa); ICE T-28-562 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 2.3 @Frequency 60 Hz | 2.3 @Frequency 60 Hz | ASTM D150 |
| Dielectric Strength | >= 21.7 kV/mm | >= 550 kV/in | ASTM D149 |
| Dissipation Factor | 0.00050 @Frequency 60 Hz | 0.00050 @Frequency 60 Hz | ASTM D150 |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | >= 170 °C | >= 338 °F | |
| Front Barrel Temperature | >= 170 °C | >= 338 °F | |
| Die Temperature | >= 185 °C | >= 365 °F | |
| Head Temperature | >= 185 °C | >= 365 °F | |