- 密度 [g/cm3]: 0.936
- 拉伸強度 [MPa]: 17.0
- 彎曲模量 [MPa]: 0.620
- 熱變形溫度 [℃]: 58.0
- 脆化溫度 [℃]: -75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.936 g/cc | 0.0338 lb/in3 | ASTM D-1505 |
| ESCR 100% Igepal? | >= 1000 hour | >= 1000 hour | Condition A, F50; ASTM D-1693 |
| ESCR 10% Igepal? | 130 hour | 130 hour | Condition A, F50; ASTM D-1693 |
| Melt Index of Compound | 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 6.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D-1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 59 | 59 | ASTM D-2240 |
| Tensile Strength, Yield | 17.0 MPa | 2470 psi | 2 in/min, Type IV bar; ASTM D-638 |
| Elongation at Break | 750 % | 750 % | 2 in/min, Type IV bar; ASTM D-638 |
| Flexural Modulus | 0.620 GPa | 89.9 ksi | 2% Secant - 16:1 span:depth, 0.5 in/min; ASTM D-790 |
| 0.760 GPa | 110 ksi | Tangent - 16:1 span:depth, 0.5 in/min; ASTM D-790 | |
| Impact Test | 102 J @Thickness 3.17 mm, Temperature -40.0 °C | 75.2 ft-lb @Thickness 0.125 in, Temperature -40.0 °F | ARM Impact |
| 237 J @Thickness 6.35 mm, Temperature -40.0 °C | 175 ft-lb @Thickness 0.250 in, Temperature -40.0 °F | ARM Impact | |
| Thermal Properties | Metric | English | Comments |
| Crystallization Temperature | 112 °C | 234 °F | ASTM D-3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 58.0 °C | 136 °F | Method A; ASTM D-648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 41.0 °C | 106 °F | Method A; ASTM D-648 |
| Vicat Softening Point | 110 °C | 230 °F | Loading 1, Rate A; ASTM D-1525 |
| Brittleness Temperature | -75.0 °C | -103 °F | Type A, Type I specimen; ASTM D-746 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 128 °C | 262 °F | ASTM D-3418 |