- 拉伸強度 [MPa]: 13.772
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.935 g/cc | 0.935 g/cc | ASTM D1928 C/D 1505 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 51 | 51 | ASTM D2240 |
| Tensile Strength, Yield | >= 13.772 MPa | >= 1997.5 psi | Heat Aging (7 days at 121°C); ASTM D638 |
| 16.2 MPa | 2350 psi | At 20 in/min; ASTM D638 | |
| Elongation at Break | 255 % | 255 % | Heat Aging (7 days at 121°C); ASTM D412 |
| 300 % | 300 % | At 20 in/min; ASTM D638 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | >= 31.5 kV/mm | >= 800 kV/in | At 40 mils; ASTM D149 |
| Track Resistance | 1.08e+6 sec | 1.08e+6 sec | Dust and Fog; ASTM D2132 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | >= 180 °C | >= 356 °F | |
| Front Barrel Temperature | >= 160 °C | >= 320 °F | |
| Die Temperature | >= 191 °C | >= 375 °F | |
| Head Temperature | >= 190 °C | >= 374 °F | |