- 熔體流動速率 [g/10min]: 48.0
- 密度 [g/cm3]: 0.9445
- 拉伸強度 [MPa]: 23.4
- 彎曲模量 [MPa]: 0.970
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.9445 g/cc | 0.03412 lb/in3 | ASTM D4883 |
| Apparent Bulk Density | 0.590 g/cc | 0.0213 lb/in3 | ASTM D1895 |
| Melt Flow | 48 g/10 min @Load 2.16 kg, Temperature 190 °C | 48 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 23.4 MPa | 3390 psi | ASTM D638 |
| Elongation at Break | <= 100 % | <= 100 % | ASTM D638 |
| Flexural Modulus | 0.970 GPa | 141 ksi | Secant; ASTM D 790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 117 °C | 243 °F | ASTM D1525 |