- 熔體流動速率 [g/10min]: 6.5
- 密度 [g/cm3]: 0.962
- 缺口沖擊強度: 0.59
- 拉伸強度 [MPa]: 36.0
- 彎曲強度 [MPa]: 14.0
- 彎曲模量 [MPa]: 1.759
- 熱變形溫度 [℃]: 77.0
- 脆化溫度 [℃]: -75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.962 g/cc | 0.0348 lb/in3 | ASTM D4883 |
| Apparent Bulk Density | 0.590 g/cc | 0.0213 lb/in3 | ASTM D1895 |
| Melt Flow | 6.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 6.5 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 66 | 66 | ASTM D2240 |
| Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638 |
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D638 |
| Elongation at Break | >= 500 % | >= 500 % | ASTM D638 |
| Flexural Modulus | 1.759 GPa | 255.1 ksi | 1% Secant; ASTM D 790 |
| Izod Impact, Notched | 0.590 J/cm | 1.11 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 77.0 °C | 171 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ASTM D648 |
| Vicat Softening Point | 131 °C | 268 °F | ASTM D1525 |
| Brittleness Temperature | <= -75.0 °C | <= -103 °F | ASTM D746 |