- 熔體流動速率 [g/10min]: 75.0
- 密度 [g/cm3]: 0.95
- 拉伸強度 [MPa]: 24.8
- 彎曲強度 [MPa]: 24.8
- 彎曲模量 [MPa]: 0.931
- 熱變形溫度 [℃]: 70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in3 | ASTM D4883 |
| Apparent Bulk Density | 0.590 g/cc | 0.0213 lb/in3 | ASTM D1895 |
| Melt Flow | 75 g/10 min @Load 2.16 kg, Temperature 190 °C | 75 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 64 | 64 | ASTM D2240 |
| Tensile Strength, Ultimate | 24.8 MPa | 3600 psi | ASTM D638 |
| Tensile Strength, Yield | 24.8 MPa | 3600 psi | ASTM D638 |
| Elongation at Break | 10 % | 10 % | ASTM D638 |
| Flexural Modulus | 0.931 GPa | 135 ksi | 2% Secant; ASTM D 790 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ASTM D648 |
| Vicat Softening Point | 115 °C | 239 °F | ASTM D1525 |