- 熔體流動速率 [g/10min]: 0.27
- 密度 [g/cm3]: 0.946
- 拉伸強度 [MPa]: 24.8
- 彎曲模量 [MPa]: 0.896
- 脆化溫度 [℃]: -75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.946 g/cc | 0.0342 lb/in3 | ASTM D1505 |
| ESCR 100% Igepal? | >= 1000 hour @Temperature 50.0 °C | >= 1000 hour @Temperature 122 °F | F0-; ASTM D1693 |
| Melt Flow | 0.27 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.27 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 66 | 66 | ASTM D2240 |
| Tensile Strength, Yield | 24.8 MPa | 3600 psi | ASTM D638 |
| Elongation at Break | >= 500 % | >= 500 % | ASTM D638 |
| Flexural Modulus | 0.896 GPa | 130 ksi | 1% Secant; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 123 °C | 253 °F | ASTM D1525 |
| Brittleness Temperature | <= -75.0 °C | <= -103 °F | ASTM D746 |