- 熔體流動速率 [g/10min]: 0.3
- 密度 [g/cm3]: 0.953
- 拉伸強度 [MPa]: 16.5
- 彎曲強度 [MPa]: 28.3
- 彎曲模量 [MPa]: 1.10
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.953 g/cc | 0.0344 lb/in3 | ASTM D4883 |
| Environmental Stress Crack Resistance | >= 24 hour | >= 24 hour | Condition B; ASTM D 1693 |
| Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.30 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 65 | 65 | ASTM D2240 |
| Tensile Strength, Ultimate | 28.3 MPa | 4100 psi | ASTM D638 |
| Tensile Strength, Yield | 16.5 MPa | 2390 psi | ASTM D638 |
| Elongation at Break | >= 600 % | >= 600 % | ASTM D638 |
| Flexural Modulus | 1.10 GPa | 160 ksi | 2% Secant; ASTM D 790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 127 °C | 261 °F | ASTM D1525 |