- 熔體流動速率 [g/10min]: 6.5
- 密度 [g/cm3]: 0.945
- 拉伸強(qiáng)度 [MPa]: 23.4
- 彎曲模量 [MPa]: 0.8273
- 脆化溫度 [℃]: -75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.945 g/cc | 0.0341 lb/in3 | ASTM D4883 |
| Apparent Bulk Density | 0.590 g/cc | 0.0213 lb/in3 | ASTM D1895 |
| Environmental Stress Crack Resistance | 40 hour | 40 hour | ASTM D1693B |
| Melt Flow | 6.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 6.5 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 23.4 MPa | 3390 psi | ASTM D638 |
| Elongation at Break | >= 1000 % | >= 1000 % | ASTM D638 |
| Flexural Modulus | 0.8273 GPa | 120.0 ksi | 1% Secant; ASTM D 790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 122 °C | 252 °F | ASTM D1525 |
| Brittleness Temperature | <= -75.0 °C | <= -103 °F | ASTM D746 |