- 熔體流動速率 [g/10min]: 0.4
- 密度 [g/cm3]: 1.1
- 拉伸強度 [MPa]: 6.89
- 彎曲強度 [MPa]: 11.0
- 脆化溫度 [℃]: -80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in3 | ASTM D1505 |
| ESCR 10% Igepal? | >= 2000 hour | >= 2000 hour | ASTM D1693 |
| Melt Flow | 0.40 g/10 min @Load 2.16 kg | 0.40 g/10 min @Load 4.76 lb | ASTM D1238 |
| 2.0 g/10 min @Load 5.00 kg | 2.0 g/10 min @Load 11.0 lb | ASTM D1238 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 59 | 59 | ASTM D2240 |
| Tensile Strength at Break | 25.0 MPa @Temperature 0.000 °C | 3630 psi @Temperature 32.0 °F | ASTM D638 |
| 25.0 MPa @Temperature -30.0 °C | 3630 psi @Temperature -22.0 °F | ASTM D638 | |
| Tensile Strength, Ultimate | 11.0 MPa @Temperature 70.0 °C | 1600 psi @Temperature 158 °F | ASTM D638 |
| Tensile Strength, Yield | 6.89 MPa @Temperature 70.0 °C | 1000 psi @Temperature 158 °F | ASTM D638 |
| 25.0 MPa @Temperature 0.000 °C | 3630 psi @Temperature 32.0 °F | ASTM D638 | |
| 30.0 MPa @Temperature -30.0 °C | 4350 psi @Temperature -22.0 °F | ASTM D638 | |
| Elongation at Break | 200 % @Temperature -30.0 °C | 200 % @Temperature -22.0 °F | ASTM D638 |
| 400 % @Temperature 0.000 °C | 400 % @Temperature 32.0 °F | ASTM D638 | |
| 500 % @Temperature 70.0 °C | 500 % @Temperature 158 °F | ASTM D638 | |
| Elongation at Yield | 4.0 % @Temperature 0.000 °C | 4.0 % @Temperature 32.0 °F | ASTM D638 |
| 4.0 % @Temperature -30.0 °C | 4.0 % @Temperature -22.0 °F | ASTM D638 | |
| 9.0 % @Temperature 70.0 °C | 9.0 % @Temperature 158 °F | ASTM D638 | |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 2.5 @Frequency 50 Hz | 2.5 @Frequency 50 Hz | ASTM D150 |
| Dielectric Strength | >= 19.7 kV/mm | >= 500 kV/in | ASTM D149 |
| Dissipation Factor | 0.00020 @Frequency 50 Hz | 0.00020 @Frequency 50 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -80.0 °C | <= -112 °F | ASTM D746 |