- 熔體流動速率 [g/10min]: 1.7
- 密度 [g/cm3]: 0.942
- 拉伸強度 [MPa]: 13.8
- 彎曲模量 [MPa]: 0.850
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.942 g/cc | 0.0340 lb/in3 | Base; ASTM D792 |
| 0.954 g/cc | 0.0345 lb/in3 | Compound; ASTM D792 | |
| ESCR 10% Igepal? | >= 2000 hour @Temperature 50.0 °C | >= 2000 hour @Temperature 122 °F | ASTM D1693/B |
| Melt Flow | 1.7 g/10 min | 1.7 g/10 min | ASTM D1238/E |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 61 | 61 | ASTM D2240 |
| Tensile Strength at Break | 25.0 MPa | 3630 psi | ASTM D638 |
| Tensile Strength, Yield | 13.8 MPa | 2000 psi | ASTM D638 |
| Elongation at Break | 700 % | 700 % | ASTM D638 |
| Flexural Modulus | 0.850 GPa | 123 ksi | ASTM D790/1 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | >= 19.7 kV/mm | >= 500 kV/in | At 50 mils; ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | >= 210 °C | >= 410 °F | |
| Front Barrel Temperature | >= 160 °C | >= 320 °F | |
| Head Temperature | >= 210 °C | >= 410 °F | |