- 熔體流動速率 [g/10min]: 0.5
- 密度 [g/cm3]: 0.946
- 彎曲強度 [MPa]: 25.0
- 彎曲模量 [MPa]: 0.850
- 脆化溫度 [℃]: 76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.946 g/cc | 0.0342 lb/in3 | Base; ASTM D792 |
| 0.958 g/cc | 0.0346 lb/in3 | Compound; ASTM D792 | |
| ESCR 10% Igepal? | >= 2000 hour @Temperature 50.0 °C | >= 2000 hour @Temperature 122 °F | ASTM D1693/B |
| Absorption Coefficient | >= 400 | >= 400 | In kilo; ASTM D3349 |
| Carbon Black Loading | 2.5 % | 2.5 % | ASTM D1603 |
| Melt Flow | 0.50 g/10 min @Load 2.16 kg | 0.50 g/10 min @Load 4.76 lb | ASTM D1238/E |
| 2.0 g/10 min @Load 5.00 kg | 2.0 g/10 min @Load 11.0 lb | ASTM D1238/P | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 61 | 61 | ASTM D2240 |
| Tensile Strength, Ultimate | >= 25.0 MPa | >= 3630 psi | ASTM D638 |
| Elongation at Break | >= 700 % | >= 700 % | ASTM D638 |
| Flexural Modulus | 0.850 GPa | 123 ksi | ASTM D790/1 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | >= 19.7 kV/mm | >= 500 kV/in | At 50 mils; ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= 76.0 °C | <= 169 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | >= 235 °C | >= 455 °F | |
| Front Barrel Temperature | >= 180 °C | >= 356 °F | |
| Head Temperature | >= 235 °C | >= 455 °F | |