- 熔體流動速率 [g/10min]: 0.5
- 密度 [g/cm3]: 0.942
- 拉伸強度 [MPa]: 13.8
- 彎曲模量 [MPa]: 0.850
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.942 g/cc | 0.0340 lb/in3 | Base Resin; ASTM D792 | ||
| Melt Flow | 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.50 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238/E | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 61 | 61 | ASTM D2240 | ||
| Tensile Strength, Yield | 13.8 MPa | 2000 psi | At 50 mm/min; ASTM D638 | ||
| Elongation at Break | 700 % | 700 % | At 50 mm/min; ASTM D638 | ||
| Flexural Modulus | 0.850 GPa | 123 ksi | ASTM D790 | ||
| Electrical Properties | Metric | English | Comments | ||
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 | ||
| Dielectric Strength | >= 19.7 kV/mm | >= 500 kV/in | At 50 mils; ASTM D3755 | ||
| Thermal Properties | Metric | English | Comments | ||
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | ASTM D746 | ||
| Descriptive Properties | |||||
| Pressure Test at High Temp | <10% | IEC 60811-3-1, Pressure Test at High Temperature (115°C, 6 hours) | |||