- 熔體流動速率 [g/10min]: 0.3
- 密度 [g/cm3]: 0.958
- 拉伸強度 [MPa]: 29.0
- 彎曲模量 [MPa]: 1.40
- 熱變形溫度 [℃]: 80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.958 g/cc | 0.0346 lb/in3 | ISO 1183 |
| Environmental Stress Crack Resistance | 100 hour | 100 hour | Antarox 10%, F50; ASTM D1693-A |
| Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.30 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| 1.3 g/10 min @Load 5.00 kg, Temperature 190 °C | 1.3 g/10 min @Load 11.0 lb, Temperature 374 °F | ISO 1133 | |
| 28 g/10 min @Load 21.6 kg, Temperature 190 °C | 28 g/10 min @Load 47.6 lb, Temperature 374 °F | ISO 1133 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 65 | 65 | ISO 868 |
| Tensile Strength, Yield | 29.0 MPa | 4210 psi | 50mm/min; ISO 527-2 |
| Elongation at Yield | 8.0 % | 8.0 % | 50mm/min; ISO 527-2 |
| Tensile Modulus | 1.30 GPa | 189 ksi | 1mm/min; ISO 527-2 |
| Flexural Modulus | 1.40 GPa | 203 ksi | 1mm/min; ISO 178 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 80.0 °C | 176 °F | ISO 75-2 |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | 170 - 190 °C | 338 - 374 °F | |
| Die Temperature | 175 - 190 °C | 347 - 374 °F | |
| Melt Temperature | 170 - 200 °C | 338 - 392 °F | |