- 熔體流動(dòng)速率 [g/10min]: 0.7
- 密度 [g/cm3]: 0.965
- 拉伸強(qiáng)度 [MPa]: 32.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.965 g/cc | 0.0349 lb/in3 | ISO 1183 |
| Environmental Stress Crack Resistance | 15 hour | 15 hour | Antarox 10%, F50; ASTM D1693-A |
| Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.70 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| 60 g/10 min @Load 21.6 kg, Temperature 190 °C | 60 g/10 min @Load 47.6 lb, Temperature 374 °F | ISO 1133 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | 50mm/min; ISO 527-2 |
| Elongation at Yield | 7.0 % | 7.0 % | 50mm/min; ISO 527-2 |
| Tensile Modulus | 1.55 GPa | 225 ksi | 1mm/min; ISO 527-2 |
| Charpy Impact, Notched | 0.700 J/cm2 @Temperature 23.0 °C | 3.33 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | 180 - 220 °C | 356 - 428 °F | |
| Die Temperature | 180 - 220 °C | 356 - 428 °F | |
| Melt Temperature | 180 - 220 °C | 356 - 428 °F | |