- 熔體流動速率 [g/10min]: 0.25
- 密度 [g/cm3]: 0.922
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in3 | ASTM D792 |
| Thickness | 38.0 microns | 1.50 mil | |
| Melt Flow | 0.25 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.25 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 15.2 MPa | 2200 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 10.0 MPa | 1450 psi | ASTM D882 |
| Film Elongation at Yield, MD | 110 % | 110 % | ASTM D882 |
| Film Elongation at Yield, TD | 450 % | 450 % | ASTM D882 |
| Coefficient of Friction | <= 0.20 | <= 0.20 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 7.80 g/micron | 198 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 3.20 g/micron | 81.3 g/mil | ASTM D1922 |
| Dart Drop | 6.30 g/micron | 160 g/mil | ASTM D1709/A |
| Film Tensile Strength at Break, MD | 29.0 MPa | 4200 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 23.1 MPa | 3350 psi | ASTM D882 |
| 1% Secant Modulus, MD | 193 MPa | 28000 psi | ASTM D882 |
| 1% Secant Modulus, TD | 228 MPa | 33000 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 30 % | 30 % | ASTM D1003 |
| Gloss | 20 % | 20 % | at 45°; ASTM D2457 |