- 熔體流動速率 [g/10min]: 7.0
- 密度 [g/cm3]: 0.924
- 拉伸強度 [MPa]: 12.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in3 | ASTM D 792 |
| Melt Flow | 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 7.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 54 | 54 | ASTM D 2240 |
| Tensile Strength at Break | 11.0 MPa | 1600 psi | ASTM D 638 |
| Tensile Strength, Yield | 12.0 MPa | 1740 psi | ASTM D 638 |
| Elongation at Break | 500 % | 500 % | ASTM D 638 |
| 1% Secant Modulus | 345 MPa | 50000 psi | ASTM D 790 |
| 2% Secant Modulus | 0.305 GPa | 44.2 ksi | ASTM D 790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 97.0 °C | 207 °F | ASTM D 1525 |