- 熔體流動速率 [g/10min]: 2.3
- 密度 [g/cm3]: 0.918
- 拉伸強度 [MPa]: 8.8
- 彎曲模量 [MPa]: 0.296
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in3 | ASTM D792 |
| Thickness | 38.0 microns | 1.50 mil | |
| Melt Flow | 2.3 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.3 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 10.0 MPa | 1450 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 8.96 MPa | 1300 psi | ASTM D882 |
| Tensile Strength, Yield | 8.80 MPa | 1280 psi | ASTM D638 |
| Film Elongation at Yield, MD | 350 % | 350 % | ASTM D882 |
| Film Elongation at Yield, TD | 550 % | 550 % | ASTM D882 |
| Elongation at Break | 712 % | 712 % | ASTM D638 |
| Flexural Modulus | 0.296 GPa | 42.9 ksi | 0.01; ASTM D790 |
| Puncture Energy | 1.71 J | 1.26 ft-lb | NOVA test |
| Coefficient of Friction | >= 0.60 | >= 0.60 | ASTM D1894 |
| Elmendorf Tear Strength MD | 225 g | 225 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 150 g | 150 g | ASTM D1922 |
| Dart drop Test | 90.0 g | 0.198 lb | F50; ASTM D1709/A |
| Film Tensile Strength at Break, MD | 17.9 MPa | 2600 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 15.9 MPa | 2300 psi | ASTM D882 |
| 1% Secant Modulus, MD | 152 MPa | 22000 psi | ASTM D882 |
| 1% Secant Modulus, TD | 176 MPa | 25500 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 12 % | 12 % | ASTM D1003 |
| Gloss | 40 % | 40 % | at 45°; ASTM D2457 |