- 熔體流動速率 [g/10min]: 2.2
- 密度 [g/cm3]: 0.923
- 拉伸強度 [MPa]: 10.3
- 彎曲強度 [MPa]: 9.7
- 脆化溫度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.923 g/cc | 0.0333 lb/in3 | Pellet; ASTM D792 |
| Melt Flow | 2.2 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.2 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 49 | 49 | ASTM D2240 |
| Tensile Strength, Ultimate | 9.70 MPa | 1410 psi | ASTM D638 |
| Tensile Strength, Yield | 10.3 MPa | 1490 psi | ASTM D638 |
| Elongation at Break | 600 % | 600 % | ASTM D638 |
| Secant Modulus | 0.193 GPa | 28.0 ksi | ASTM D638 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+18 ohm-cm | 1.00e+18 ohm-cm | ASTM D257 |
| Dielectric Constant | 2.28 @Frequency 1e+6 Hz | 2.28 @Frequency 1e+6 Hz | ASTM D1531 |
| Dissipation Factor | 0.00010 @Frequency 1e+6 Hz | 0.00010 @Frequency 1e+6 Hz | ASTM D1531 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 110 °C | 230 °F | NOVA |
| Vicat Softening Point | 92.0 °C | 198 °F | ASTM D1525 |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D746 |