- 熔體流動速率 [g/10min]: 2.2
- 密度 [g/cm3]: 0.924
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in3 | ASTM D792 |
| Thickness | 38.0 microns | 1.50 mil | |
| Melt Flow | 2.2 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.2 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 11.0 MPa | 1600 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 9.65 MPa | 1400 psi | ASTM D882 |
| Film Elongation at Yield, MD | 330 % | 330 % | ASTM D882 |
| Film Elongation at Yield, TD | 520 % | 520 % | ASTM D882 |
| Coefficient of Friction | <= 0.15 | <= 0.15 | ASTM D1894 |
| Elmendorf Tear Strength MD | 228 g | 228 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 264 g | 264 g | ASTM D1922 |
| Dart drop Test | 120 g | 0.265 lb | F50; ASTM D1709/A |
| Film Tensile Strength at Break, MD | 20.99 MPa | 3045 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 15.00 MPa | 2175 psi | ASTM D882 |
| 1% Secant Modulus, MD | 215 MPa | 31200 psi | ASTM D882 |
| 1% Secant Modulus, TD | 220 MPa | 31900 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 6.5 % | 6.5 % | ASTM D1003 |
| Gloss | 70 % | 70 % | at 45°; ASTM D2457 |
| Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified |