- 熔體流動速率 [g/10min]: 7.0
- 密度 [g/cm3]: 0.917
- 拉伸強度 [MPa]: 9.0
- 彎曲模量 [MPa]: 0.211
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in3 | ASTM D 792 |
| Melt Flow | 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 7.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 53 | 53 | ASTM D 2240 |
| Tensile Strength at Break | 11.0 MPa | 1600 psi | ASTM D 638 |
| Tensile Strength, Yield | 9.00 MPa | 1310 psi | ASTM D 638 |
| Elongation at Break | 548 % | 548 % | ASTM D 638 |
| Flexural Modulus | 0.211 GPa | 30.6 ksi | 2% Secant; ASTM D 790 |
| Flexural Modulus, 1% Secant | 236 MPa | 34200 psi | ASTM D 790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 83.0 °C | 181 °F | ASTM D 1525 |