- 熔體流動速率 [g/10min]: 2.3
- 密度 [g/cm3]: 0.921
- 彎曲強度 [MPa]: 10.3
- 彎曲模量 [MPa]: 0.200
- 脆化溫度 [℃]: -72.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in3 | Exxon Method |
| Environmental Stress Crack Resistance | <= 1.0 hour | <= 1.0 hour | F50, Condition A; ASTM D-1693 |
| Melt Flow | 2.3 g/10 min | 2.3 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 45 | 45 | ASTM D2240 |
| Tensile Strength, Ultimate | 10.3 MPa | 1490 psi | ASTM D638 |
| Elongation at Break | 600 % | 600 % | ASTM D638 |
| Flexural Modulus | 0.200 GPa | 29.0 ksi | ASTM D790 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 2.26 @Frequency 1e+6 Hz | 2.26 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 21.0 kV/mm @Thickness 3.17 mm | 533 kV/in @Thickness 0.125 in | ASTM D149 |
| Dissipation Factor | 0.00010 @Frequency 1e+6 Hz | 0.00010 @Frequency 1e+6 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 109 °C | 228 °F | Exxon Method |
| Brittleness Temperature | <= -72.0 °C | <= -97.6 °F | ASTM D746 |