- 熔體流動速率 [g/10min]: 0.75
- 密度 [g/cm3]: 0.921
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in3 | Exxon Method |
| Thickness | 31.8 microns | 1.25 mil | |
| Melt Flow | 0.75 g/10 min | 0.75 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 12.0 MPa | 1740 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 11.0 MPa | 1600 psi | ASTM D882 |
| Film Elongation at Break, MD | 120 % | 120 % | ASTM D882 |
| Film Elongation at Break, TD | 600 % | 600 % | ASTM D882 |
| Secant Modulus, MD | 0.230 GPa | 33.4 ksi | ASTM D882 |
| Secant Modulus, TD | 0.320 GPa | 46.4 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 450 g | 450 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 80 g | 80 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 14.2 g/micron | 360 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 2.52 g/micron | 64.0 g/mil | ASTM D1922 |
| Dart Drop | 2.52 g/micron | 64.0 g/mil | F50; ASTM D1709 |
| Dart drop Test | 80.0 g | 0.176 lb | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 35.0 MPa | 5080 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 21.0 MPa | 3050 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 108 °C | 226 °F | Exxon Method |
| Optical Properties | Metric | English | Comments |
| Haze | 14 % | 14 % | ASTM D1003 |
| Gloss | 45 % | 45 % | 45°, ASTM D-2457 |