- 熔體流動速率 [g/10min]: 1.3
- 密度 [g/cm3]: 0.924
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in3 | Exxon Method |
| Thickness | 31.8 microns | 1.25 mil | |
| Melt Flow | 1.3 g/10 min | 1.3 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 11.0 MPa | 1600 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 12.0 MPa | 1740 psi | ASTM D882 |
| Film Elongation at Break, MD | 250 % | 250 % | ASTM D882 |
| Film Elongation at Break, TD | 600 % | 600 % | ASTM D882 |
| Secant Modulus, MD | 0.260 GPa | 37.7 ksi | ASTM D882 |
| Secant Modulus, TD | 0.280 GPa | 40.6 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 400 g | 400 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 150 g | 150 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 12.6 g/micron | 320 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 4.72 g/micron | 120 g/mil | ASTM D1922 |
| Dart Drop | 1.57 g/micron | 40.0 g/mil | F50; ASTM D1709 |
| Dart drop Test | 50.0 g | 0.110 lb | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 31.0 MPa | 4500 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 20.0 MPa | 2900 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 112 °C | 234 °F | Exxon Method |
| Optical Properties | Metric | English | Comments |
| Haze | 5.0 % | 5.0 % | ASTM D1003 |
| Gloss | 75 % | 75 % | 45°, ASTM D-2457 |