- 密度 [g/cm3]: 0.919
- 拉伸強度 [MPa]: 11.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in3 | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 89 | 89 | 15s; ASTM D2240 |
| Hardness, Shore D | 42 | 42 | 15s; ASTM D2240 |
| Tensile Strength at Break | 7.58 MPa | 1100 psi | ASTM D638 |
| Tensile Strength, Yield | 11.0 MPa | 1600 psi | ASTM D638 |
| Elongation at Break | 200 % | 200 % | ASTM D638 |
| Elongation at Yield | 30 % | 30 % | ASTM D638 |
| 1% Secant Modulus | 234 MPa | 34000 psi | ASTM D790 |
| Impact Test | 17.6 J | 13.0 ft-lb | @ -4oF, Instrumented Impact Total Energy; ASTM D3763 |
| 23.0 J | 17.0 ft-lb | @ 73oF, Instrumented Impact Total Energy at -20°C; ASTM D3763 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 110 °C | 230 °F | Peak Melting Temperature; ExxonMobil Method |
| Vicat Softening Point | 86.1 °C | 187 °F | ASTM D1525 |