- 熔體流動速率 [g/10min]: 6.3
- 密度 [g/cm3]: 0.921
- 拉伸強度 [MPa]: 12.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in3 | ExxonMobil Method |
| Melt Flow | 6.3 g/10 min | 6.3 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 82 | 82 | 15s; ASTM D2240 |
| Hardness, Shore D | 43 | 43 | 15s; ASTM D2240 |
| Tensile Strength at Break | 9.86 MPa | 1430 psi | ASTM D638 |
| Tensile Strength, Yield | 12.2 MPa | 1770 psi | ASTM D638 |
| Elongation at Break | 440 % | 440 % | ASTM D638 |
| Elongation at Yield | 24 % | 24 % | ASTM D638 |
| 1% Secant Modulus | 255 MPa | 37000 psi | ASTM D790 |
| Impact Test | 19.0 J | 14.0 ft-lb | Instrumented Impact Total Energy; ASTM D3763 |
| 35.3 J | 26.0 ft-lb | Instrumented Impact Total Energy at -40°C; ASTM D3763 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 110 °C | 230 °F | Peak Melting Temperature; ExxonMobil Method |
| Vicat Softening Point | 93.9 °C | 201 °F | ASTM D1525 |