- 熔體流動速率 [g/10min]: 33.0
- 密度 [g/cm3]: 0.921
- 拉伸強度 [MPa]: 12.4
- 彎曲模量 [MPa]: 248
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in3 | ExxonMobil Method | ||
| Melt Flow | 33 g/10 min @Load 2.16 kg, Temperature 190 °C | 33 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 81 @Time 15.0 sec | 81 @Time 0.00417 hour | ASTM D2240 | ||
| Hardness, Shore D | 49 | 49 | 15s; ASTM D2240 | ||
| Tensile Strength at Break | 8.27 MPa | 1200 psi | ASTM D638 | ||
| Tensile Strength, Yield | 12.4 MPa | 1800 psi | ASTM D638 | ||
| Elongation at Break | 130 % | 130 % | ASTM D638 | ||
| Elongation at Yield | 20 % | 20 % | ASTM D638 | ||
| Flexural Modulus, 1% Secant | 248 MPa | 36000 psi | ASTM D790 | ||
| Dart Drop, Total Energy | 16.3 J @Temperature 22.8 °C | 12.0 ft-lb @Temperature 73.0 °F | ASTM D3763 | ||
| 24.4 J @Temperature -20.0 °C | 18.0 ft-lb @Temperature -4.00 °F | ASTM D3763 | |||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 91.1 °C | 196 °F | ASTM D1525 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||