- 熔體流動速率 [g/10min]: 2.3
- 密度 [g/cm3]: 0.918
- 拉伸強度 [MPa]: 10.3
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in3 | ExxonMobil Method |
| Melt Flow | 2.3 g/10 min | 2.3 g/10 min | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 84 | 84 | 15s; ASTM D2240 |
| Hardness, Shore D | 48 | 48 | 15s; ASTM D2240 |
| Tensile Strength at Break | 9.65 MPa | 1400 psi | ASTM D638 |
| Tensile Strength, Yield | 10.3 MPa | 1500 psi | at 2% Offset; ASTM D638 |
| Elongation at Break | >= 800 % | >= 800 % | ASTM D638 |
| Elongation at Yield | 33 % | 33 % | ASTM D638 |
| 1% Secant Modulus | 207 MPa | 30000 psi | ASTM D790 |
| Impact Test | 9.90 - 18.0 J | 7.30 - 13.3 ft-lb | Instrumented Impact Total Energy; ASTM D3763 |
| 15.5 - 24.5 J | 11.4 - 18.1 ft-lb | Instrumented Impact Total Energy at -20°C; ASTM D3763 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 110 °C | 230 °F | Peak Melting Temperature; ExxonMobil Method |
| Vicat Softening Point | 86.7 °C | 188 °F | ASTM D1525 |