- 熔體流動速率 [g/10min]: 6.5
- 密度 [g/cm3]: 0.922
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in3 | Exxon Method |
| Thickness | 12.7 microns | 0.500 mil | |
| Melt Flow | 6.5 g/10 min | 6.5 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 200 % | 200 % | ASTM D882 |
| Film Elongation at Break, TD | 450 % | 450 % | ASTM D882 |
| Secant Modulus, MD | 0.207 GPa | 30.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.225 GPa | 32.6 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 190 g | 190 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 90 g | 90 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 15.0 g/micron | 380 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 7.09 g/micron | 180 g/mil | ASTM D1922 |
| Dart Drop | <= 3.15 g/micron | <= 80.0 g/mil | F50; ASTM D1709 |
| Dart drop Test | <= 40.0 g | <= 0.0882 lb | F50; ASTM D1709 |
| Film Tensile Strength at Break, MD | 23.0 MPa | 3340 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 15.0 MPa | 2180 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 110 °C | 230 °F | Exxon Method |
| Optical Properties | Metric | English | Comments |
| Haze | 5.4 % | 5.4 % | ASTM D1003 |
| Gloss | 74 % | 74 % | 45°, ASTM D-2457 |