- 熔體流動速率 [g/10min]: 3.75
- 密度 [g/cm3]: 0.92
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in3 | ExxonMobil Method | ||
| Thickness | 38.1 microns | 1.50 mil | |||
| Melt Flow | 3.75 g/10 min | 3.75 g/10 min | ExxonMobil Method | ||
| Antiblock Level | 1200 ppm | 1200 ppm | |||
| Slip Level | 900 ppm | 900 ppm | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 9.38 MPa | 1360 psi | at 2% offset; ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 9.58 MPa | 1390 psi | at 2% offset; ASTM D882 | ||
| Film Elongation at Break, MD | 200 % | 200 % | ASTM D882 | ||
| Film Elongation at Break, TD | 560 % | 560 % | ASTM D882 | ||
| Film Elongation at Yield, MD | 6.4 % | 6.4 % | ASTM D882 | ||
| Film Elongation at Yield, TD | 5.5 % | 5.5 % | ASTM D882 | ||
| Elmendorf Tear Strength MD | 260 g | 260 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 140 g | 140 g | ASTM D1922 | ||
| Elmendorf Tear Strength, MD | 6.823 g/micron | 173.3 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 3.67 g/micron | 93.3 g/mil | ASTM D1922 | ||
| Dart Drop | 2.36 g/micron | 60.0 g/mil | ASTM D1709 | ||
| Dart drop Test | 90.0 g | 0.198 lb | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 21.2 MPa | 3080 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 18.3 MPa | 2650 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 176 MPa | 25500 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 212 MPa | 30800 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 108 °C | 226 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Crystallization Temperature | 95.0 °C | 203 °F | ExxonMobil Method | ||
| Vicat Softening Point | 91.7 °C | 197 °F | ASTM D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 5.5 % | 5.5 % | ASTM D1003 | ||
| Gloss | 73 % | 73 % | 45°; ASTM D2457 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.