- 熔體流動速率 [g/10min]: 2.1
- 密度 [g/cm3]: 0.923
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.923 g/cc | 0.0333 lb/in3 | ExxonMobil Method | ||
| Thickness | 38.1 microns | 1.50 mil | |||
| Melt Flow | 2.1 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.1 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Antiblock Level | 1500 ppm | 1500 ppm | |||
| Slip Level | 750 ppm | 750 ppm | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 11.0 MPa | 1600 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 11.0 MPa | 1600 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 190 % | 190 % | ASTM D882 | ||
| Film Elongation at Break, TD | 550 % | 550 % | ASTM D882 | ||
| Puncture Energy | 0.463 J | 0.342 ft-lb | ExxonMobil Method | ||
| Elmendorf Tear Strength MD | 380 g | 380 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 160 g | 160 g | ASTM D1922 | ||
| Dart drop Test | 80.0 g | 0.176 lb | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 24.1 MPa | 3500 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 20.0 MPa | 2900 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 207 MPa | 30000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 248 MPa | 36000 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 111 °C | 232 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 6.2 % | 6.2 % | ASTM D1003 | ||
| Gloss | 72 % | 72 % | 45°; ASTM D2457 | ||
| Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||