- 熔體流動速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.923
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.923 g/cc | 0.0333 lb/in3 | ExxonMobil Method | ||
| Thickness | 38.1 microns | 1.50 mil | |||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Antiblock Level | 1000 ppm | 1000 ppm | |||
| Slip Level | 750 ppm | 750 ppm | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 11.0 MPa | 1600 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 11.0 MPa | 1600 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 210 % | 210 % | ASTM D882 | ||
| Film Elongation at Break, TD | 570 % | 570 % | ASTM D882 | ||
| Puncture Energy | 0.757 J | 0.558 ft-lb | ExxonMobil Method | ||
| Elmendorf Tear Strength MD | 350 g | 350 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 190 g | 190 g | ASTM D1922 | ||
| Dart drop Test | 100 g | 0.221 lb | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 24.9 MPa | 3610 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 21.4 MPa | 3100 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 214 MPa | 31000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 255 MPa | 37000 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 111 °C | 232 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 5.2 % | 5.2 % | ASTM D1003 | ||
| Gloss | 76 % | 76 % | 45°; ASTM D2457 | ||
| Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||