- 熔體流動速率 [g/10min]: 3.0
- 密度 [g/cm3]: 0.921
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in3 | ExxonMobil Method | ||
| Thickness | 38.1 microns | 1.50 mil | |||
| Melt Flow | 3.0 g/10 min | 3.0 g/10 min | ExxonMobil Method | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 10.1 MPa | 1460 psi | at 2% offset; ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 10.3 MPa | 1490 psi | at 2% offset; ASTM D882 | ||
| Film Elongation at Break, MD | 340 % | 340 % | ASTM D882 | ||
| Film Elongation at Break, TD | 640 % | 640 % | ASTM D882 | ||
| Film Elongation at Yield, MD | 6.2 % | 6.2 % | ASTM D882 | ||
| Film Elongation at Yield, TD | 5.4 % | 5.4 % | ASTM D882 | ||
| Elmendorf Tear Strength MD | 310 g | 310 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 180 g | 180 g | ASTM D1922 | ||
| Elmendorf Tear Strength, MD | 8.134 g/micron | 206.6 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 4.72 g/micron | 120 g/mil | ASTM D1922 | ||
| Dart Drop | 2.62 g/micron | 66.6 g/mil | ASTM D1709 | ||
| Dart drop Test | 100 g | 0.221 lb | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 26.3 MPa | 3820 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 21.3 MPa | 3090 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 192 MPa | 27800 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 230 MPa | 33400 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 109 °C | 228 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 4.4 % | 4.4 % | ASTM D1003 | ||
| Gloss | 80 % | 80 % | 45°; ASTM D2457 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.